POLYETHYLENE COMPOUND
Description
PolyAzin-E 410C is a high-density polyethylene compound containing 5% calcium carbonate. This compound is designed to offer a unique combination of easy extrusion and high melt strength, along with excellent mechanical performance. It is particularly suitable for producing thin films with outstanding strength and rigidity. The grade is naturally colored and also available in custom colors upon request. Additionally, we offer tailor-made compounds based on customer-specific technical requirements.
Properties
| Physical | Typical Value | Unit | Test Method |
| Melt Flow Rate (190°C/ 5 kg) | 0.4 | g/10min | ISO 1133 |
| Density | 0.97 | g/cm3 | ISO 1183 |
| Mechanical | Typical Value | Unit | Test Method |
| Flexural Modulus | 1000 | N/mm2 | ISO 178 |
| Tensile Strength at Yield | 23 | N/mm2 | ISO 527 |
| Elongation at Yield | 8 | % | ISO 527 |
| Hardness shore D | 66 | Points | ISO 868 |
* This data is provided for reference only and is not intended for specification use.
Advantages
- Excellent mechanical and physical properties
- Good processability
- High melt strength
- Good stiffness
Applications
- Counter bags
- Film extrusion
- Carrier bag
Processing Guidlines
- Recommended process: Blown film extrusion, Cast film extrusion
- Pre-drying: Not required under normal storage conditions, but if moisture is suspected, drying at 70°C for 2-3 hours is recommended.
- Processing temperature range: 180-210°C (depending on equipment and die design)
Note: Actual parameters should be optimized for your specific line and targeted applications.
Packaging & Storage
For optimal performance, Use within 6 months from production date
Supplied in 25 kg bags or 850 kg jumbo bags in granular form
Store in a dry, cool environment; avoid UV exposure and humidity