GLASS FIBER REINFORCED POLYPROPYLENE COMPOUND
Description
PolyAzin-M 530G2 is a polypropylene-based compound reinforced with 30% glass fiber, designed for injection molding applications. The glass fibers are chemically coupled to the polymer matrix, resulting in significantly improved mechanical properties such as strength, stiffness, and dimensional stability, while keeping the material lightweight. This grade also exhibits excellent chemical resistance, enhanced heat-resistant, and reduced thermal expansion compared to unfilled polypropylene. This grade is naturally colored and also available in custom colors upon request. Additionally, we offer tailor-made compounds based on customer-specific technical requirements.
Properties
| Physical | Typical Value | Unit | Test Method |
| Melt Flow Rate (230°C/2.16kg) | 6 | g/10min | ISO 1133 |
| Density | 1.12 | g/cm3 | ISO 1183 |
| Mechanical | Typical Value | Unit | Test Method |
| Flexural Modulus | 5600 | N/mm2 | ISO 178 |
| Tensile Strength at break | 90 | N/mm2 | ISO 527 |
| Elongation at break | 5 | % | ISO 527 |
| IZOD Impact Strength (Notch) at 23 °C | 17 | KJ/m2 | ISO 180 |
| Hardness shore D | 78 | Points | ISO 868 |
| Thermal | Typical Value | Unit | Test Method |
| H.D.T. (1.82 MPa) | 157 | °C | ISO 75-2 |
* This data is provided for reference only and is not intended for specification use.
Advantages
- Excellent mechanical properties
- Good impact resistance
- Easy processing and good flowability
- High chemical and thermal resistance
- Low weight alternative to metal or filled materials
Application
- Home appliances
- Automotive components
- Packaging industry
- Industrial parts
Processing Guidlines
- Recommended process: Injection molding
- Pre-drying: Not required under normal storage conditions, but if moisture is suspected, drying at 80°C for 2-3 hours is recommended.
- Processing temperature range: 180-240°C (depending on equipment and die design)
Note: Actual parameters should be optimized for your specific line and targeted applications.
Performance may vary depending on polymer grade, processing equipment, and operating
conditions. Pre-testing is recommended
Packaging & Storage
For optimal performance, Use within 6 months from production date
Supplied in 25 kg bags or 850 kg jumbo bags in granular form
Store in a dry, cool environment; avoid UV exposure and humidity