HIGH IMPACT POLYPROPYLENE COMPOUND FOR BUMPERS
Description
PolyAzin-N 500 is a non-filled polypropylene compound designed for injection molding applications. It offers good UV stabilization and excellent mechanical properties with a well-balanced combination of stiffness and impact strength. It is naturally colored and also available in custom colors upon request. Additionally, we offer tailor-made compounds based on customer-specific technical requirements.
Properties
| Physical | Typical Value | Unit | Test Method |
| Melt Flow Rate (230°C/2.16kg) | 10 | g/10min | ISO 1133 |
| Density | 0.9 | g/cm3 | ISO 1183 |
| Mechanical | Typical Value | Unit | Test Method |
| Flexural Modulus | 1000 | N/mm2 | ISO 178 |
| Tensile Strength at Yield | 21 | N/mm2 | ISO 527 |
| Tensile Strength at break | ≥ 15 | N/mm2 | ISO 527 |
| Elongation at Yield | 4 | % | ISO 527 |
| Elongation at break | ≥ 300 | % | ISO 527 |
| IZOD Impact Strength (Notch) at 23 °C | ≥ 50 | KJ/m2 | ISO 180 |
| Hardness shore D | 56 | Points | ISO 868 |
* This data is provided for reference only and is not intended for specification use.
Advantages
- Very high impact strength
- Good UV resistance
- Good processability
Applications
- Automotive bumper
- Automotive parts
- Injection moulded components
Processing Guidlines
- Recommended process: Injection molding
- Pre-drying: Recommended at 80°C for 2-4 hours to minimize moisture-related defects.
- Processing temperature range: 180-230°C (depending on equipment and die design)
Note: Actual parameters should be optimized for your specific production line and end-use application.
Packaging & Storage
For optimal performance, Use within 6 months from production date
Supplied in 25 kg bags or 850 kg jumbo bags in granular form
Store in a dry, cool environment; avoid UV exposure and humidity